Fuel electrode for solid electrolyte fuel cells and a method for manufacture of the electrode

ABSTRACT

The invention relates to a fuel electrode for high-temperature solid electrolyte fuel cells and a process for manufacture of the electrode. The fuel electrode of the invention is a porous element composed of a high-melting metal, such as ruthenium, osmium, rhodium or iridium, or an alloy containing the metal. The process for manufacture of the fuel electrode comprises coating an electrode material with a solution or dispersion of the high-melting metal and/or its chloride, sintering the same and finally reducing the product.

BACKGROUND OF THE INVENTION

The present invention relates to a fuel electrode for high-temperature solid electrolyte fuel cells and a method for manufacture of the electrode.

Heretofore, nickel/zirconia (Ni/ZrO₂) cermets have been employed for fuel electrodes in commercialized high-temperature solid electrolyte fuel cells.

These Ni/ZrO₂ cermets are typically produced by the following alternative processes: (1) A process in which NiO/ZrO₂ is sintered and then reduced to provide a Ni/ZrO₂ cermet (e.g. the Ceramatec process described in Proceedings of SOFC-NAGOYA, p. 24); (2) A process, known as the Westinghouse process, in which ZrO₂ in a crude Ni/ZrO₂ cermet is caused to grow into spaces between Ni grains by the EVD technique (Japanese Kokai Patent Publication No. 61-153280).

Aside from the above, porous platinum (Pt) materials obtainable by sintering platinum pastes have been used in ZrO₂ sensors and the like or in basic research.

However, the Ni/ZrO₂ cermet electrode manufactured by the first-mentioned process is disadvantageous in that when the fuel cell is run over thousands of hours at temperatures near 1,000° C., the Ni grains therein are sintered to degrade the electrode and ultimately cause exfoliation of the electrode. Increasing the proportion of ZrO₂ for avoiding this sintering detracts from the performance of the electrode.

The Ni/ZrO₂ cermet manufactured by the second-mentioned process is resistant to sintering and insures a satisfactory electrode performance but since it involves an EVD step, the overall manufacturing process is complicated and the cost of manufacture is increased.

The porous platinum electrode is disadvantageous in that the platinum reacts with impure metal in the fuel and is vaporized in a continuous operation in a reducing atmosphere to cause early aging of the electrode. Furthermore, platinum is an expensive metal and the manufacture of porous platinum electrodes is costly.

SUMMARY OF THE INVENTION

The object of the present invention is to overcome the above disadvantages and provide an improved fuel electrode which does not undergo sintering or aging even when the fuel cell is operated continuously for a long time at a high temperature and a simple method for manufacture of the electrode.

The fuel electrode of the invention for high-temperature solid electrolyte fuel cells is characterized in that it is a porous element composed of a high-melting metal having a melting point of not less than 1,900° C. or an alloy containing such a high-melting metal.

As species of the high-melting metal with a melting point of not less than 1,900° C., there may be mentioned ruthenium (Ru), osmium (Os), rhodium (Rh) and iridium (Ir).

As apparent from the melting points presented below, Ru, Os, Rh and Ir melt at higher temperatures than Ni and Pt and are more resistant to sintering. Because they are highly resistant to sintering, ceramication is not required. Furthermore, since the resistance to sintering is high, it is feasible to design a system with a long interfacial dimension of the three-phase zone of ZrO₂ /Metal/GAS (if such a structure is designed with Ni, sintering occurs soon) and thereby reduce all the reaction polarization, diffusion polarization and resistance polarization of the electrode.

    ______________________________________                                         Melting points                                                                 ______________________________________                                                 Ni          1453° C.                                                    Pt          1769° C.                                                    Ru          2500° C.                                                    Rh          1960° C.                                                    Ir          2443° C.                                                    Os          2700° C.                                            ______________________________________                                    

Of the above-mentioned metals, Ru is the most advantageous in having:

(1) A high melting point and stability even in a reducing atmosphere;

(2) Low cost; and

(3) High catalyst activity for steam reforming of CH₄ which is an important factor in electrode performance.

Osmium (Os) is also useful but in view of the high vapor pressure of OsO₄ and its high toxicity, it is somewhat handicapped for commercial exploitation as compared with Ru.

The fuel electrode of the present invention for high-temperature solid electrolyte fuel cells can be manufactured by dissolving or dispersing at least one of powdery Ru, Os, Rh and Ir or at least one of ruthenium chloride, osmium chloride, rhodium chloride and iridium chloride in an organic solvent or water, coating an electrode material with the resulting solution or dispersion, sintering the same and finally reducing it. It should be understood that such powdery metal and metal chloride may be used in combination.

The sintering operation is preferably conducted in an oxidizing atmosphere at a temperature of 400°˜1,000° C. and the reduction reaction is preferably conducted at a temperature of 500°˜1,300° C.

Preferably the reduction is conducted in a reducing atmosphere, particularly in a hydrogen (H₂) atmosphere.

The organic solvent to be used is preferably a low-boiling solvent and more desirably an alcohol of 1 to 6 carbon atoms. The most advantageous are propanol and butanol.

In terms of the ease of porosity control and handling, it is good practice to employ a high molecular compound soluble in the organic solvent or in water. Among such high molecular compounds are polybutyl alcohol, polyvinyl alcohol and methylellulose.

Compared with the conventional Ni/ZrO₂ cermet electrode, the electrode according to the present invention has the following meritorious characteristics:

(1) Substantially no sintering occurs even when the fuel cell is run for thousands of hours at 1,000° C.;

(2) Each of the reaction, diffusion and resistance polarization values are as small as several mV at 200 mA/cm².

Particularly when Ru is employed, not only an excellent electrode performance is insured but the manufacturing cost is low resulting in profitable commercial application.

Furthermore, since the manufacturing method according to the present invention is a simple process comprising coating an electrode material with an aqueous or organic solution or dispersion of a powdery high-melting metal and/or a high-melting metal chloride, sintering the same and, then, reducing it, the manufacturing process is simple and the cost of manufacture is low. Moreover, the concomitant use of a high molecular compound soluble in the organic solvent or water facilities porosity control and handling.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The following examples and comparative examples are intended to illustrate the invention in further detail and should by no means be construed as defining the metes and bounds of the invention.

Example 1

In 89 parts by weight of n-butanol were dissolved 10 parts by weight of hydrous ruthenium trichloride (RuCl₃.3H₂ O) and 1 part by weight of polybutyl alcohol, and pellets (2 cm in diameter and 0.2 mm thick) of yttria-doped zirconia (ZrO₂ containing 8 mol % of Y₂ O₃ ; hereinafter referred to as YSZ) were coated with the resulting solution. The coated pellets were heated in air at 850° C. and, then, reduced in a H₂ atmosphere at 1,000° C. to provide a porous electrode having a thickness of 50 μm. Using this as the fuel electrode, a fuel cell was fabricated and a fuel gas composed of 90 vol % of H₂ and 10 vol % of H₂ O and the air were passed to the fuel electrode and the air electrode, respectively, to investigate the polarization characteristics at 200 mA/cm². As a result, all the reaction, diffusion and resistance polarization values were not larger than 5 mV. The same fuel electrode was maintained in H₂ streams at 1,000° C. for 1,315 hours and similar determinations were made. As a result, no significant difference was found in any of these parameter values.

Example 2

To 30 parts by weight of a 5% aqueous solution of polyvinyl alcohol was added 70 parts by weight of powdery ruthenium metal (particle size 1˜5 μm) followed by thorough mixing. Then, YSZ pellets were coated with the resulting slurry. The coated pellets were heated in the air at 500° C. (for removal of the binder) and, then, reduced in streams of a gas composed of 5 vol % of H₂ and 95 vol % of N₂ at 1,050° C. to provide a porous electrode having a thickness of 50 μm. The performance of this electrode was comparable to that of the electrode obtained in Example 1.

Example 3

In 89 parts by weight of water were dissolved 10 parts by weight of hydrous ruthenium trichloride and 1 part by weight of polyvinyl alcohol. YSZ pellets were coated with the resulting solution and, thereafter, the procedure described in Example 2 was repeated to provide an electrode. The performance of this electrode was comparable to that of the electrode obtained in Example 1.

Example 4

In 35 parts by weight of a 5% aqueous solution of polyvinyl alcohol was dissolved 3 parts by weight of ruthenium chloride followed by addition of 62 parts by weight of powdery ruthenium metal to prepare a slurry. YSZ pellets were coated with the above slurry and the coated pellets were dried at room temperature and heated in the air at 500° C. Then, the pellets were reduced in streams of a gas composed of 5 vol % of H₂ and 95 vol % of N₂ at 1,050° C. The characteristics of the resulting electrode (about 50 μm thick) were similar to those of the electrode obtained in Example 1.

Comparative Example 1

A 70 weight % suspension of powdery NiO plus powdery YSZ (NiO:YSZ=6:4, w/w) in ethanol was used to coat the same YSZ pellets as used in Example 1. The coated pellets were sintered in the air at 1,300° C. and, then, reduced in a hydrogen stream at 1,000° C. to provide a Ni/ZrO₂ cermet electrode. This electrode was tested for various parameters as in Example 1. As a result, the sum of reaction polarization and diffusion polarization values at 200 mA/cm² was 30˜100 mV. When the same electrode was maintained in a stream of H₂ at 1,000° C. for 1,050 hours, extensive exfoliation took place. 

What is claimed is:
 1. A high-temperature solid electrolyte fuel cell comprising a porous fuel electrode and an air electrode, said porous fuel electrode consisting essentially of an electrode material and high-melting metal having a melting point of not less than 1,900° C., wherein said high-melting is at least one member selected from the group consisting of ruthenium, osmium, rhodium, iridium and alloys thereof.
 2. A fuel cell according to claim 1, wherein said high-melting metal consists of ruthenium metal.
 3. A fuel cell according to claim 1, wherein said electrode material consists essentially of yttria-doped zirconia.
 4. A process for manufacturing a fuel electrode for a high temperature solid electrolyte fuel cell by the steps of dissolving or dispersing at least one member selected from the group consisting of ruthenium, osmium, rhodium, iridium, and chlorides thereof in a solvent selected from the group consisting of an organic solvent selected from a low boiling point solvent and an alcohol having 1 to 6 carbon atoms, and water, coating an electrode material with the resulting solution or dispersion, sintering the coated electrode material, and then reducing said coated material.
 5. A process according to claim 1, wherein the solvent further includes a high molecular compound dissolved therein.
 6. A process according to claim 4, wherein said sintering is performed at 400° to 1,000° C. and said reducing is performed at 500° to 1,300° C.
 7. A process according to claim 1 wherein said solvent is an alcohol having from 1 to 6 carbon atoms.
 8. A process according to claim 2, wherein said solvent is an alcohol having from 1 to 6 carbon atoms.
 9. A process according to claim 2, wherein said solvent is water.
 10. A process according to claim 9, wherein said high molecular compound is polyvinyl alcohol.
 11. A process according to claim 4, wherein said electrode material consists essentially of yttria-doped zirconia.
 12. A process according to claim 4, wherein said sintering is performed in an oxidizing atmosphere, and said reducing is performed in a reducing atmosphere.
 13. A process according to claim 12, wherein said reducing atmosphere is a hydrogen atmosphere.
 14. A process according to claim 8, wherein said organic solvent is n-butanol and said high molecular compound is polybutyl alcohol. 